METAL CR-NI MAGNUM CERAMIC S X UNID
$1.904
Material: Cromo – NÃquel
Uso: Cerámico
¿POR QUÉ USARLA?
- Facilidad de fusión
- Poca oxidación
- Elaboración sencilla
- Excelente pulido y consistencia
- Elevada compatibilidad con diferentes revestimientos estéticos
Descripción
Composition in %
Nickel (Ni) 63 % Chrome (Cr) 25 % Molybdenum (Mo) 9 % Silicon (Si) 2 %
Physical and mechanical features
| Solidus-liquidus temperature | 1298 ÷ 1344 °C |
| Thermal expansion coefficient | (25 ÷ 500 °C) 13,7 x 10-6 K-1 – (25 ÷ 600 °C) 14 x 10-6 K-1 |
| Melting point | 1400 °C |
| Density | 8,3 g/cmc |
| Vickers hardness | 180 HV10 |
| Percentage elongation at fracture | 26 % |
| Yield load strength | (Rp0.2) 360 MPa |
| Modulus of elasticity | 191 GPa |
| Ions release in 7 days | 1,8 μg/cm2 |
| Maximium cooking temperature | 950°C |
| Colour | White |